H150(LF) /H150(LF)Q

特性/ Features

耐CAF性能

Anti-CAF capability

UV Blocking与(yu) AOI兼(jian)容可提高PCB生产效率

UV Blocking and AOI compatible,so as to increase productivity efficiency

优异的耐热(re)性,Td ≥325℃,T288≥5min ,适合于无(wu)铅焊工艺;

High thermal performance,Td ≥325℃ ,T288≥5min,suitable for lead-free process。

 

应用领域/ Applications 

计(ji)算机及外围设备(bei)、通讯设备(bei)、汽(qi)车电子。

computer, communication equipment, Automotive electronics.

 

主要特性 / General properties

检测项目

Item

单位

Unit

检测条件

Test   Condition

测(ce)试方法IPC-TM-650

典型(xing)值(zhi)

Typical   Value

玻(bo)璃化(hua)转变温度Tg

DSC

 2.4.25

154.5

剥(bo)离强度 1oz Peel Strength

N/mm

288℃, 10S

2.4.8

1.41

热应(ying)力

Thermal stress

S

288℃,solder dip

2.4.13.1

180 s

No delamination

弯曲强度

Flexural Strength

N/mm2

LW/CW

 2.4.4

570/465

燃烧性

Flammability

Rating

E 24/125

UL94

V-0

表面电阻

Surface Resistivity

After moisture

2.5.17.1

6.12×107

体积电(dian)阻(zu)

Volume   Resistivity

MΩ·cm

After moisture

2.5.17.1

6.25×108

介(jie)电常数

Dielectric   Constant

1 GHz

C 24/23/50

2.5.5.9

4.7

介质损耗角正切

Loss   Tangent

1 GHz

C 24/23/50

2.5.5.9

0.016

耐电弧

Arc Resistance

S

D48/50D0.5/23

2.5.1

125

击穿(chuan)电压

Dielectric Breakdown 

KV

D48/50D0.5/23

2.5.6

57

吸水(shui)率

Moisture Absorption

%

D-24/23

2.6.2.1

0.10

热(re)分解温度Td

Weight Loss 5%

2.2.24.6

358

CTE

Z-axis

Alpha 1

ppm / ℃

 

TMA

2.4.24

55

Alpha 2

ppm / ℃

2.4.24

276

50 - 260 ℃

%

2.4.24

3.3

T288

min

TMA

2.4.24.1

30

相比漏电起痕(hen)指(zhi)数 CTI

Rating

C-96/20/65

IEC-60112

PLC 3

Specimen Thickness : 1.6mm ;   Specification sheet:IPC-4101D/99,is for your reference only


半固化(hua)片介绍(shao)-H150P(LF)/ H150P(LF)Q

H150P (LF) / H150P(LF)QUV Prepreg

prepreg   type

Resin   Content(%)

压合厚度Cured thickness(mm/mil)

R/C(%)含量(liang)

公(gong)差(cha)Tolerance

Nominal

Range(±)mil

%

±

mm

mil

mm

mil

7628HRC

52

2

0.231

9.09

0.022

0.9

50

2

0.220

8.66

0.022

0.9

48

2

0.210

8.27

0.02

0.8

7628

45

2

0.195

7.68

0.019

0.8

43

2

0.186

7.32

0.018

0.7

1506

50

2

0.173

6.80

0.017

0.7

48

2

0.164

6.46

0.017

0.6

2116

60

2

0.145

5.71

0.015

0.6

58

2

0.136

5.35

0.014

0.5

55

2

0.125

4.92

0.013

0.5

53

2

0.119

4.69

0.011

0.5

1080

70

2

0.092

3.62

0.009

0.4

68

2

0.086

3.39

0.008

0.3

65

2

0.079

3.11

0.008

0.3

63

2

0.073

2.87

0.008

0.3

106

75

2

0.056

2.20

0.006

0.2

73

2

0.052

2.05

0.005

0.2

71

2

0.050

1.97

0.005

0.2


建议压制程式:
 Suggest cycle

442f4b9ab53c3c888f2f34ec0e18ffe0.png

储存条件(jian)温度(du)≤23℃、湿度(du)≤50%,保(bao)存(cun)时间3个月;温度≤5℃、密封(feng)条件下,保(bao)存时(shi)间6个(ge)月(yue).

Storage Condition: T≤23℃& ≤50%RH,Within 3 months;  T≤5 ℃ Within 6 months (seal condition).

在(zai)上述要求内(nei),我(wo)司可(ke)立即安排PP送样;若有特(te)殊要求,由供需双方(fang)商(shang)定。Follow above condition,

Our company will arrange sample immediately. We can discuss if you have special requirement.